For rust protection of embedded parts, angle iron, lamp posts, railings, fences, and other metal components.

Phone:

+86-020-62315158

Request a quote

Download

Still hesitating? Get a sample first, contact us!

Category:

Anti Corrosion Application

Keywords:

Product Description

Sysmyk ^® Water-based zinc-plated

[Product Code] TCP0002

[Product Features]

TCP0002 is an advanced patented technology for galvanizing steel developed by Hysenmec (Patent No.: CN107033642B). This technology requires only a simple, one-time dip-coating process combined with rapid heating, enabling the quick deposition of a bright, electroplating-like zinc-based protective coating onto the steel surface. The coating utilizes a newly developed water-based nanoparticle from Hysenmec, which exhibits strong hydrophobic properties and effectively repels moisture to the exterior of the coating without compromising the metallic texture of the coating. At the same time, this nanoparticle significantly enhances wear resistance and dramatically improves corrosion protection performance.

◼ Heavy-metal-free, water-based system, green galvanizing

◼ After curing, the coating exhibits both high hardness and a certain degree of flexibility.

■ Hardness of 4H or higher, with excellent wear resistance.

◼ Over 500 hours of neutral salt spray performance (in combination with zinc infiltration process)

◼ Patent technology ensures product quality.

[Applicable Materials]

Metal workpiece anti-corrosion surface treatment

【Curing Method】

Baking temperature: Pre-bake at 70°C for 10 minutes; cure at 160°C for 30 minutes (workpiece temperature).

【Scope of Application】

Embedded parts, angle iron, lamp posts, railings, fences, etc.
[Technical Parameters]

[Techniques and Precautions]

◼ Construction process:

Note: The number of dip-coating applications can be flexibly adjusted according to the rust-prevention requirements; it can be either one or two applications.

◼ Instructions for Use and Precautions

1. Open TCP0002 and disperse it using an electric stirrer for 2 minutes. Then, add deionized water to TCP0002 at a ratio of 10–15%. Ensure the viscosity is controlled within the range of 17–20 seconds (measured with a #4 cup at 25°C). After thoroughly mixing, transfer the mixture into the material tank. During use, if the viscosity becomes too high, add the corresponding dedicated diluent to adjust the viscosity back to 17–20 seconds (measured with a #4 cup at 25°C).

2. The production area using TCP0002 requires forced ventilation.

3. The surface of the workpiece to be processed must be free of dirt and oil contamination.

4. The TCP0002 galvanizing solution must be diluted with deionized water.

5. The baking temperature for TCP0002 coating is too low, resulting in incomplete crosslinking; if the temperature is too high, the coating will become powdery, causing TCP0002 coating to lose its anti-corrosion performance. Please bake the TCP0002 coating within the temperature range specified in the product instructions.

6. The shelf life of TCP0002 is 2-3 months, so it should be used up as soon as possible.

[Storage]

Recommended storage temperature: 18–25°C Shelf life: 3 months

[Packaging]
20 kg/barrel

[Environmental Protection]

Safety recommendations/transportation regulations—please refer to the product’s MSDS manual.